Brand Name : TANKII
Model Number : 0Cr27Al7Mo2/
Certification : ISO9001
Place of Origin : China
MOQ : 20kg
Price : negotiation
Payment Terms : L/C, T/T, Western Union
Supply Ability : 20, 000kg/month
Delivery Time : 5-10 days
Packaging Details : On Spool,In Coil
Application : Industry
Shape : rod/bar/round material
Material : FeCrAl
Chemical composition : Ferro Chrome Aluminium
Surface : Bright,acid white/oxidized
FeCrAl( 0Cr27Al7Mo2) resistance alloy
With the characteristics of high resistance, low coefficient of electric resistance, high operating temperature, good corrosion resistance under high temperature, it is widely used in the single crystal furnace, sintering furnace, ceramic calcining furnace and heat treatment furnace.
0Cr27Al7Mo2
Chemical Content(%)
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other | ||
Max | |||||||||||
0.05 | 0.025 | 0.025 | 0.20 | Max 0.40 | 26.5~27.8 | Max 0.60 | 5.0~7.0 | Bal. | Mo 1.8-2.2 |
Mechanical Properties
Max Continuous Service Temp | 1350ºC |
Resisivity at 20ºC | 1.45 ohm mm2/m |
Density | 7.1 g/cm3 |
Thermal Conductivity | 46.1 KJ/m·h·ºC |
Coefficient of Thermal Expansion | 16.0×10-6/ºC |
Melting Point | 1510ºC |
Tensile Strength | 637~784 Mpa |
Elongation | Min 12% |
Section Variation Shrink Rate | 65~75% |
Repeatedly Bend Frequency | Min 5 times |
Continuous Service Time | - |
Hardness | 200-260HB |
Micrographic Structure | Ferrite |
Magnetic Property | Magnetic |
Temperature Factor of Electrical Resistivity
20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 500ºC | 600ºC | 700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1200ºC |
1 | 0.997 | 0.996 | 0.994 | 0.991 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 |
0Cr27Al7Mo2 FeCrAl Alloy FeCrAl Heating Rod For Thermocouple Images |